EN 1.8151 Steel vs. 5652 Aluminum

EN 1.8151 steel belongs to the iron alloys classification, while 5652 aluminum belongs to the aluminum alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.8151 steel and the bottom bar is 5652 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 540
47 to 77
Elastic (Young's, Tensile) Modulus, GPa 190
68
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 72
26
Tensile Strength: Ultimate (UTS), MPa 670 to 1940
190 to 290

Thermal Properties

Latent Heat of Fusion, J/g 270
400
Maximum Temperature: Mechanical, °C 410
190
Melting Completion (Liquidus), °C 1440
650
Melting Onset (Solidus), °C 1400
610
Specific Heat Capacity, J/kg-K 480
900
Thermal Conductivity, W/m-K 50
140
Thermal Expansion, µm/m-K 13
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
35
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
120

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
9.5
Density, g/cm3 7.7
2.7
Embodied Carbon, kg CO2/kg material 1.8
8.6
Embodied Energy, MJ/kg 25
150
Embodied Water, L/kg 49
1190

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
51
Strength to Weight: Axial, points 24 to 70
20 to 30
Strength to Weight: Bending, points 22 to 45
27 to 36
Thermal Diffusivity, mm2/s 14
57
Thermal Shock Resistance, points 20 to 58
8.4 to 13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
95.8 to 97.7
Carbon (C), % 0.4 to 0.5
0
Chromium (Cr), % 0.4 to 0.8
0.15 to 0.35
Copper (Cu), % 0
0 to 0.040
Iron (Fe), % 95.9 to 97.2
0 to 0.4
Magnesium (Mg), % 0
2.2 to 2.8
Manganese (Mn), % 0.6 to 0.9
0 to 0.010
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 1.3 to 1.7
0 to 0.4
Sulfur (S), % 0 to 0.025
0
Vanadium (V), % 0.1 to 0.2
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15

Comparable Variants