EN 1.8151 Steel vs. 6060 Aluminum

EN 1.8151 steel belongs to the iron alloys classification, while 6060 aluminum belongs to the aluminum alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.8151 steel and the bottom bar is 6060 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
68
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 72
26
Tensile Strength: Ultimate (UTS), MPa 670 to 1940
140 to 220

Thermal Properties

Latent Heat of Fusion, J/g 270
400
Maximum Temperature: Mechanical, °C 410
160
Melting Completion (Liquidus), °C 1440
660
Melting Onset (Solidus), °C 1400
610
Specific Heat Capacity, J/kg-K 480
900
Thermal Conductivity, W/m-K 50
210
Thermal Expansion, µm/m-K 13
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
54
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
180

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
9.5
Density, g/cm3 7.7
2.7
Embodied Carbon, kg CO2/kg material 1.8
8.3
Embodied Energy, MJ/kg 25
150
Embodied Water, L/kg 49
1190

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
50
Strength to Weight: Axial, points 24 to 70
14 to 23
Strength to Weight: Bending, points 22 to 45
22 to 30
Thermal Diffusivity, mm2/s 14
85
Thermal Shock Resistance, points 20 to 58
6.3 to 9.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
97.9 to 99.3
Carbon (C), % 0.4 to 0.5
0
Chromium (Cr), % 0.4 to 0.8
0 to 0.050
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 95.9 to 97.2
0.1 to 0.3
Magnesium (Mg), % 0
0.35 to 0.6
Manganese (Mn), % 0.6 to 0.9
0 to 0.1
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 1.3 to 1.7
0.3 to 0.6
Sulfur (S), % 0 to 0.025
0
Titanium (Ti), % 0
0 to 0.1
Vanadium (V), % 0.1 to 0.2
0
Zinc (Zn), % 0
0 to 0.15
Residuals, % 0
0 to 0.15