MakeItFrom.com
Menu (ESC)

EN 1.8151 Steel vs. AWS BAg-1

EN 1.8151 steel belongs to the iron alloys classification, while AWS BAg-1 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.8151 steel and the bottom bar is AWS BAg-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
75
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 72
28
Tensile Strength: Ultimate (UTS), MPa 670 to 1940
170

Thermal Properties

Latent Heat of Fusion, J/g 270
110
Melting Completion (Liquidus), °C 1440
620
Melting Onset (Solidus), °C 1400
610
Specific Heat Capacity, J/kg-K 480
280
Thermal Expansion, µm/m-K 13
23

Otherwise Unclassified Properties

Density, g/cm3 7.7
9.2
Embodied Carbon, kg CO2/kg material 1.8
44
Embodied Energy, MJ/kg 25
690

Common Calculations

Stiffness to Weight: Axial, points 13
4.6
Stiffness to Weight: Bending, points 25
15
Strength to Weight: Axial, points 24 to 70
5.1
Strength to Weight: Bending, points 22 to 45
7.4
Thermal Shock Resistance, points 20 to 58
7.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0
23 to 25
Carbon (C), % 0.4 to 0.5
0
Chromium (Cr), % 0.4 to 0.8
0
Copper (Cu), % 0
14 to 16
Iron (Fe), % 95.9 to 97.2
0
Manganese (Mn), % 0.6 to 0.9
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 1.3 to 1.7
0
Silver (Ag), % 0
44 to 46
Sulfur (S), % 0 to 0.025
0
Vanadium (V), % 0.1 to 0.2
0
Zinc (Zn), % 0
14 to 18
Residuals, % 0
0 to 0.15