EN 1.8151 Steel vs. EN 1.6982 Stainless Steel

Both EN 1.8151 steel and EN 1.6982 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.8151 steel and the bottom bar is EN 1.6982 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
76
Tensile Strength: Ultimate (UTS), MPa 670 to 1940
800

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Maximum Temperature: Mechanical, °C 410
770
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 50
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
10
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 1.8
2.4
Embodied Energy, MJ/kg 25
33
Embodied Water, L/kg 49
110

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24 to 70
28
Strength to Weight: Bending, points 22 to 45
25
Thermal Diffusivity, mm2/s 14
6.6
Thermal Shock Resistance, points 20 to 58
29

Alloy Composition

Carbon (C), % 0.4 to 0.5
0 to 0.050
Chromium (Cr), % 0.4 to 0.8
12 to 13.5
Iron (Fe), % 95.9 to 97.2
78.7 to 84.5
Manganese (Mn), % 0.6 to 0.9
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.7
Nickel (Ni), % 0
3.5 to 5.0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 1.3 to 1.7
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015
Vanadium (V), % 0.1 to 0.2
0