EN 1.8151 Steel vs. EN 2.4964 Cobalt

EN 1.8151 steel belongs to the iron alloys classification, while EN 2.4964 cobalt belongs to the cobalt alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.8151 steel and the bottom bar is EN 2.4964 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
86
Tensile Strength: Ultimate (UTS), MPa 670 to 1940
960

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Melting Completion (Liquidus), °C 1440
1630
Melting Onset (Solidus), °C 1400
1550
Specific Heat Capacity, J/kg-K 480
400
Thermal Conductivity, W/m-K 50
15
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
1.8

Otherwise Unclassified Properties

Density, g/cm3 7.7
9.6
Embodied Carbon, kg CO2/kg material 1.8
9.8
Embodied Energy, MJ/kg 25
140
Embodied Water, L/kg 49
450

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 25
21
Strength to Weight: Axial, points 24 to 70
28
Strength to Weight: Bending, points 22 to 45
23
Thermal Diffusivity, mm2/s 14
3.9
Thermal Shock Resistance, points 20 to 58
25

Alloy Composition

Carbon (C), % 0.4 to 0.5
0.050 to 0.15
Chromium (Cr), % 0.4 to 0.8
19 to 21
Cobalt (Co), % 0
46.4 to 58
Iron (Fe), % 95.9 to 97.2
0 to 3.0
Manganese (Mn), % 0.6 to 0.9
0 to 2.0
Nickel (Ni), % 0
9.0 to 11
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 1.3 to 1.7
0 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.015
Tungsten (W), % 0
14 to 16
Vanadium (V), % 0.1 to 0.2
0