EN 1.8151 Steel vs. SAE-AISI T4 Steel

Both EN 1.8151 steel and SAE-AISI T4 steel are iron alloys. They have 71% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.8151 steel and the bottom bar is SAE-AISI T4 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
80
Tensile Strength: Ultimate (UTS), MPa 670 to 1940
800 to 2140

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Melting Completion (Liquidus), °C 1440
1810
Melting Onset (Solidus), °C 1400
1750
Specific Heat Capacity, J/kg-K 480
410
Thermal Conductivity, W/m-K 50
21
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
55
Density, g/cm3 7.7
9.4
Embodied Carbon, kg CO2/kg material 1.8
8.5
Embodied Energy, MJ/kg 25
130
Embodied Water, L/kg 49
120

Common Calculations

Stiffness to Weight: Axial, points 13
12
Stiffness to Weight: Bending, points 25
21
Strength to Weight: Axial, points 24 to 70
24 to 64
Strength to Weight: Bending, points 22 to 45
20 to 39
Thermal Diffusivity, mm2/s 14
5.4
Thermal Shock Resistance, points 20 to 58
24 to 64

Alloy Composition

Carbon (C), % 0.4 to 0.5
0.7 to 0.8
Chromium (Cr), % 0.4 to 0.8
3.8 to 4.5
Cobalt (Co), % 0
4.3 to 5.8
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 95.9 to 97.2
66.3 to 72.3
Manganese (Mn), % 0.6 to 0.9
0.1 to 0.4
Molybdenum (Mo), % 0
0.4 to 1.0
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 1.3 to 1.7
0.2 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.030
Tungsten (W), % 0
17.5 to 19
Vanadium (V), % 0.1 to 0.2
0.8 to 1.2

Comparable Variants