EN 1.8151 Steel vs. N06035 Nickel

EN 1.8151 steel belongs to the iron alloys classification, while N06035 nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.8151 steel and the bottom bar is N06035 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
84
Tensile Strength: Ultimate (UTS), MPa 670 to 1940
660

Thermal Properties

Latent Heat of Fusion, J/g 270
340
Maximum Temperature: Mechanical, °C 410
1030
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
450
Thermal Expansion, µm/m-K 13
13

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
60
Density, g/cm3 7.7
8.4
Embodied Carbon, kg CO2/kg material 1.8
10
Embodied Energy, MJ/kg 25
140
Embodied Water, L/kg 49
330

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24 to 70
22
Strength to Weight: Bending, points 22 to 45
20
Thermal Shock Resistance, points 20 to 58
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.4
Carbon (C), % 0.4 to 0.5
0 to 0.050
Chromium (Cr), % 0.4 to 0.8
32.3 to 34.3
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 95.9 to 97.2
0 to 2.0
Manganese (Mn), % 0.6 to 0.9
0 to 0.5
Molybdenum (Mo), % 0
7.6 to 9.0
Nickel (Ni), % 0
51.1 to 60.2
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 1.3 to 1.7
0 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.015
Tungsten (W), % 0
0 to 0.6
Vanadium (V), % 0.1 to 0.2
0 to 0.2