MakeItFrom.com
Menu (ESC)

EN 1.8151 Steel vs. N10276 Nickel

EN 1.8151 steel belongs to the iron alloys classification, while N10276 nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.8151 steel and the bottom bar is N10276 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
84
Tensile Strength: Ultimate (UTS), MPa 670 to 1940
780

Thermal Properties

Latent Heat of Fusion, J/g 270
320
Maximum Temperature: Mechanical, °C 410
960
Melting Completion (Liquidus), °C 1440
1370
Melting Onset (Solidus), °C 1400
1320
Specific Heat Capacity, J/kg-K 480
410
Thermal Conductivity, W/m-K 50
9.1
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
1.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
70
Density, g/cm3 7.7
9.1
Embodied Carbon, kg CO2/kg material 1.8
13
Embodied Energy, MJ/kg 25
170
Embodied Water, L/kg 49
280

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 24 to 70
24
Strength to Weight: Bending, points 22 to 45
21
Thermal Diffusivity, mm2/s 14
2.4
Thermal Shock Resistance, points 20 to 58
23

Alloy Composition

Carbon (C), % 0.4 to 0.5
0 to 0.010
Chromium (Cr), % 0.4 to 0.8
14.5 to 16.5
Cobalt (Co), % 0
0 to 2.5
Iron (Fe), % 95.9 to 97.2
4.0 to 7.0
Manganese (Mn), % 0.6 to 0.9
0 to 0.010
Molybdenum (Mo), % 0
15 to 17
Nickel (Ni), % 0
51 to 63.5
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 1.3 to 1.7
0 to 0.080
Sulfur (S), % 0 to 0.025
0 to 0.030
Tungsten (W), % 0
3.0 to 4.5
Vanadium (V), % 0.1 to 0.2
0 to 0.35