EN 1.8151 Steel vs. S36200 Stainless Steel

Both EN 1.8151 steel and S36200 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.8151 steel and the bottom bar is S36200 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
76
Tensile Strength: Ultimate (UTS), MPa 670 to 1940
1180 to 1410

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Maximum Temperature: Mechanical, °C 410
820
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 50
16
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
12
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 1.8
2.8
Embodied Energy, MJ/kg 25
40
Embodied Water, L/kg 49
120

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24 to 70
42 to 50
Strength to Weight: Bending, points 22 to 45
32 to 36
Thermal Diffusivity, mm2/s 14
4.3
Thermal Shock Resistance, points 20 to 58
40 to 48

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0.4 to 0.5
0 to 0.050
Chromium (Cr), % 0.4 to 0.8
14 to 14.5
Iron (Fe), % 95.9 to 97.2
75.4 to 79.5
Manganese (Mn), % 0.6 to 0.9
0 to 0.5
Molybdenum (Mo), % 0
0 to 0.3
Nickel (Ni), % 0
6.5 to 7.0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 1.3 to 1.7
0 to 0.3
Sulfur (S), % 0 to 0.025
0 to 0.030
Titanium (Ti), % 0
0.6 to 0.9
Vanadium (V), % 0.1 to 0.2
0

Comparable Variants