EN 1.8152 Steel vs. EN 2.4816 Nickel

EN 1.8152 steel belongs to the iron alloys classification, while EN 2.4816 nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.8152 steel and the bottom bar is EN 2.4816 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 540
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
74
Tensile Strength: Ultimate (UTS), MPa 660 to 2010
700

Thermal Properties

Latent Heat of Fusion, J/g 270
310
Maximum Temperature: Mechanical, °C 410
1150
Melting Completion (Liquidus), °C 1440
1370
Melting Onset (Solidus), °C 1400
1320
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 47
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
1.8

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
55
Density, g/cm3 7.7
8.5
Embodied Carbon, kg CO2/kg material 1.8
9.0
Embodied Energy, MJ/kg 25
130
Embodied Water, L/kg 49
260

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 24 to 72
23
Strength to Weight: Bending, points 22 to 46
21
Thermal Diffusivity, mm2/s 13
3.8
Thermal Shock Resistance, points 20 to 60
20

Alloy Composition

Aluminum (Al), % 0
0 to 0.3
Carbon (C), % 0.51 to 0.59
0.050 to 0.1
Chromium (Cr), % 0.5 to 0.8
14 to 17
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 96 to 97.2
6.0 to 10
Manganese (Mn), % 0.5 to 0.8
0 to 1.0
Nickel (Ni), % 0
72 to 80
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 1.2 to 1.6
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.015
Titanium (Ti), % 0
0 to 0.3
Vanadium (V), % 0.1 to 0.2
0