MakeItFrom.com
Menu (ESC)

EN 1.8503 Steel vs. Zamak 7

EN 1.8503 steel belongs to the iron alloys classification, while Zamak 7 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.8503 steel and the bottom bar is Zamak 7.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 300
80
Elastic (Young's, Tensile) Modulus, GPa 190
86
Elongation at Break, % 16
13
Fatigue Strength, MPa 600
47
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 73
33
Shear Strength, MPa 610
210
Tensile Strength: Ultimate (UTS), MPa 1000
280
Tensile Strength: Yield (Proof), MPa 910
250

Thermal Properties

Latent Heat of Fusion, J/g 250
120
Maximum Temperature: Mechanical, °C 440
95
Melting Completion (Liquidus), °C 1470
390
Melting Onset (Solidus), °C 1420
380
Specific Heat Capacity, J/kg-K 470
410
Thermal Conductivity, W/m-K 41
110
Thermal Expansion, µm/m-K 13
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
38

Otherwise Unclassified Properties

Base Metal Price, % relative 3.3
11
Density, g/cm3 7.8
6.4
Embodied Carbon, kg CO2/kg material 2.3
3.0
Embodied Energy, MJ/kg 33
57
Embodied Water, L/kg 57
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
36
Resilience: Unit (Modulus of Resilience), kJ/m3 2200
370
Stiffness to Weight: Axial, points 13
7.5
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 35
12
Strength to Weight: Bending, points 28
15
Thermal Diffusivity, mm2/s 11
43
Thermal Shock Resistance, points 29
8.6

Alloy Composition

Aluminum (Al), % 0 to 0.3
3.5 to 4.3
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0.16 to 0.24
0
Chromium (Cr), % 1.2 to 1.5
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 95.8 to 97.5
0 to 0.075
Lead (Pb), % 0
0 to 0.0030
Magnesium (Mg), % 0
0.0050 to 0.020
Manganese (Mn), % 0.4 to 0.8
0
Molybdenum (Mo), % 0.65 to 0.8
0
Nickel (Ni), % 0
0.0050 to 0.020
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.035
0
Tin (Sn), % 0
0 to 0.0010
Vanadium (V), % 0.25 to 0.35
0
Zinc (Zn), % 0
95.3 to 96.5