EN 1.8522 Steel vs. ASTM A369 Grade FP92

Both EN 1.8522 steel and ASTM A369 grade FP92 are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.8522 steel and the bottom bar is ASTM A369 grade FP92.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 380
210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
76
Tensile Strength: Ultimate (UTS), MPa 730 to 1250
710

Thermal Properties

Latent Heat of Fusion, J/g 260
260
Maximum Temperature: Mechanical, °C 470
590
Melting Completion (Liquidus), °C 1460
1490
Melting Onset (Solidus), °C 1420
1450
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
26
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
9.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
10

Otherwise Unclassified Properties

Base Metal Price, % relative 4.2
11
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.2
2.8
Embodied Energy, MJ/kg 31
40
Embodied Water, L/kg 63
89

Common Calculations

PREN (Pitting Resistance) 6.2
14
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26 to 44
25
Strength to Weight: Bending, points 23 to 33
22
Thermal Diffusivity, mm2/s 11
6.9
Thermal Shock Resistance, points 21 to 36
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0.0010 to 0.0060
Carbon (C), % 0.29 to 0.36
0.070 to 0.13
Chromium (Cr), % 2.8 to 3.3
8.5 to 9.5
Copper (Cu), % 0 to 0.1
0
Iron (Fe), % 93.7 to 96
85.8 to 89.1
Manganese (Mn), % 0.4 to 0.7
0.3 to 0.6
Molybdenum (Mo), % 0.7 to 1.2
0.3 to 0.6
Nickel (Ni), % 0 to 0.3
0 to 0.4
Niobium (Nb), % 0
0.040 to 0.090
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.4
0 to 0.5
Sulfur (S), % 0 to 0.035
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
1.5 to 2.0
Vanadium (V), % 0.15 to 0.25
0.15 to 0.25
Zirconium (Zr), % 0
0 to 0.010