EN 1.8818 Steel vs. AISI 410S Stainless Steel

Both EN 1.8818 steel and AISI 410S stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.8818 steel and the bottom bar is AISI 410S stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 27
25
Fatigue Strength, MPa 200
180
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 280
310
Tensile Strength: Ultimate (UTS), MPa 440
480
Tensile Strength: Yield (Proof), MPa 270
250

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
740
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
30
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.6
1.9
Embodied Energy, MJ/kg 21
27
Embodied Water, L/kg 49
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
100
Resilience: Unit (Modulus of Resilience), kJ/m3 200
170
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
17
Strength to Weight: Bending, points 16
18
Thermal Diffusivity, mm2/s 13
8.1
Thermal Shock Resistance, points 13
17

Alloy Composition

Aluminum (Al), % 0.015 to 0.034
0
Carbon (C), % 0 to 0.15
0 to 0.080
Chromium (Cr), % 0 to 0.35
11.5 to 13.5
Copper (Cu), % 0 to 0.6
0
Iron (Fe), % 95.9 to 99.985
83.8 to 88.5
Manganese (Mn), % 0 to 1.6
0 to 1.0
Molybdenum (Mo), % 0 to 0.13
0
Nickel (Ni), % 0 to 0.35
0 to 0.6
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.017
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.55
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0 to 0.060
0
Vanadium (V), % 0 to 0.1
0