EN 1.8818 Steel vs. AWS BAg-19

EN 1.8818 steel belongs to the iron alloys classification, while AWS BAg-19 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.

For each property being compared, the top bar is EN 1.8818 steel and the bottom bar is AWS BAg-19.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
74
Poisson's Ratio 0.29
0.37
Shear Modulus, GPa 73
27
Tensile Strength: Ultimate (UTS), MPa 440
140

Thermal Properties

Latent Heat of Fusion, J/g 250
120
Melting Completion (Liquidus), °C 1460
890
Melting Onset (Solidus), °C 1420
760
Specific Heat Capacity, J/kg-K 470
250
Thermal Expansion, µm/m-K 13
20

Otherwise Unclassified Properties

Density, g/cm3 7.8
10

Common Calculations

Stiffness to Weight: Axial, points 13
4.0
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 16
3.8
Strength to Weight: Bending, points 16
5.8
Thermal Shock Resistance, points 13
6.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.015 to 0.034
0
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 0 to 0.35
0
Copper (Cu), % 0 to 0.6
6.6 to 7.9
Iron (Fe), % 95.9 to 99.985
0
Lithium (Li), % 0
0.15 to 0.3
Manganese (Mn), % 0 to 1.6
0
Molybdenum (Mo), % 0 to 0.13
0
Nickel (Ni), % 0 to 0.35
0
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.017
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 0.55
0
Silver (Ag), % 0
92 to 93
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0 to 0.060
0
Vanadium (V), % 0 to 0.1
0
Residuals, % 0
0 to 0.15