EN 1.8818 Steel vs. C55284 Copper

EN 1.8818 steel belongs to the iron alloys classification, while C55284 copper belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is EN 1.8818 steel and the bottom bar is C55284 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
100
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
38
Tensile Strength: Ultimate (UTS), MPa 440
180

Thermal Properties

Latent Heat of Fusion, J/g 250
180
Maximum Temperature: Mechanical, °C 400
200
Melting Completion (Liquidus), °C 1460
800
Melting Onset (Solidus), °C 1420
640
Specific Heat Capacity, J/kg-K 470
380
Thermal Expansion, µm/m-K 13
17

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.6
16
Embodied Energy, MJ/kg 21
260

Common Calculations

Stiffness to Weight: Axial, points 13
6.5
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 16
5.6
Strength to Weight: Bending, points 16
8.0
Thermal Shock Resistance, points 13
7.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.015 to 0.034
0
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 0 to 0.35
0
Copper (Cu), % 0 to 0.6
79.2 to 80.7
Iron (Fe), % 95.9 to 99.985
0
Manganese (Mn), % 0 to 1.6
0
Molybdenum (Mo), % 0 to 0.13
0
Nickel (Ni), % 0 to 0.35
0
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.017
0
Phosphorus (P), % 0 to 0.035
4.8 to 5.2
Silicon (Si), % 0 to 0.55
0
Silver (Ag), % 0
14.5 to 15.5
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0 to 0.060
0
Vanadium (V), % 0 to 0.1
0
Residuals, % 0
0 to 0.15