EN 1.8818 Steel vs. C87300 Bronze

EN 1.8818 steel belongs to the iron alloys classification, while C87300 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.8818 steel and the bottom bar is C87300 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 27
22
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
43
Tensile Strength: Ultimate (UTS), MPa 440
350
Tensile Strength: Yield (Proof), MPa 270
140

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
200
Melting Completion (Liquidus), °C 1460
970
Melting Onset (Solidus), °C 1420
820
Specific Heat Capacity, J/kg-K 470
410
Thermal Conductivity, W/m-K 48
28
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
6.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
6.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
29
Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 1.6
2.7
Embodied Energy, MJ/kg 21
42
Embodied Water, L/kg 49
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
62
Resilience: Unit (Modulus of Resilience), kJ/m3 200
86
Stiffness to Weight: Axial, points 13
7.5
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 16
11
Strength to Weight: Bending, points 16
13
Thermal Diffusivity, mm2/s 13
8.0
Thermal Shock Resistance, points 13
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.015 to 0.034
0
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 0 to 0.35
0
Copper (Cu), % 0 to 0.6
94 to 95.7
Iron (Fe), % 95.9 to 99.985
0 to 0.2
Lead (Pb), % 0
0 to 0.2
Manganese (Mn), % 0 to 1.6
0.8 to 1.5
Molybdenum (Mo), % 0 to 0.13
0
Nickel (Ni), % 0 to 0.35
0
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.017
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 0.55
3.5 to 5.0
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0 to 0.060
0
Vanadium (V), % 0 to 0.1
0
Zinc (Zn), % 0
0 to 0.25
Residuals, % 0
0 to 0.5