EN 1.8818 Steel vs. N08811 Stainless Steel

Both EN 1.8818 steel and N08811 stainless steel are iron alloys. They have 47% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.8818 steel and the bottom bar is N08811 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 27
33
Fatigue Strength, MPa 200
150
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 280
340
Tensile Strength: Ultimate (UTS), MPa 440
510
Tensile Strength: Yield (Proof), MPa 270
190

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1390
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
12
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.6
5.3
Embodied Energy, MJ/kg 21
76
Embodied Water, L/kg 49
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
130
Resilience: Unit (Modulus of Resilience), kJ/m3 200
94
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16
18
Strength to Weight: Bending, points 16
18
Thermal Diffusivity, mm2/s 13
3.0
Thermal Shock Resistance, points 13
13

Alloy Composition

Aluminum (Al), % 0.015 to 0.034
0.15 to 0.6
Carbon (C), % 0 to 0.15
0.060 to 0.1
Chromium (Cr), % 0 to 0.35
19 to 23
Copper (Cu), % 0 to 0.6
0 to 0.75
Iron (Fe), % 95.9 to 99.985
39.5 to 50.6
Manganese (Mn), % 0 to 1.6
0 to 1.5
Molybdenum (Mo), % 0 to 0.13
0
Nickel (Ni), % 0 to 0.35
30 to 35
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.017
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.55
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0 to 0.060
0.15 to 0.6
Vanadium (V), % 0 to 0.1
0