EN 1.8824 Steel vs. 60Cr-40Ni Alloy

EN 1.8824 steel belongs to the iron alloys classification, while 60Cr-40Ni alloy belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is EN 1.8824 steel and the bottom bar is 60Cr-40Ni alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 73
87
Tensile Strength: Ultimate (UTS), MPa 580
870
Tensile Strength: Yield (Proof), MPa 440
660

Thermal Properties

Latent Heat of Fusion, J/g 250
370
Specific Heat Capacity, J/kg-K 470
490
Thermal Expansion, µm/m-K 13
16

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
49
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
7.4
Embodied Energy, MJ/kg 21
110
Embodied Water, L/kg 48
380

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 530
1000
Stiffness to Weight: Axial, points 13
16
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 21
31
Strength to Weight: Bending, points 20
26
Thermal Shock Resistance, points 17
18

Alloy Composition

Aluminum (Al), % 0.020 to 0.040
0 to 0.25
Carbon (C), % 0 to 0.16
0 to 0.1
Chromium (Cr), % 0
58 to 62
Iron (Fe), % 96.6 to 99.98
0 to 1.0
Manganese (Mn), % 0 to 1.7
0 to 0.3
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 0 to 0.5
34.5 to 42
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.020
Titanium (Ti), % 0 to 0.050
0 to 0.5
Vanadium (V), % 0 to 0.1
0