EN 1.8824 Steel vs. 85-silver 15-nickel

EN 1.8824 steel belongs to the iron alloys classification, while 85-silver 15-nickel belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is EN 1.8824 steel and the bottom bar is 85-silver 15-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
88
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 73
32
Tensile Strength: Ultimate (UTS), MPa 580
260 to 470

Thermal Properties

Latent Heat of Fusion, J/g 250
140
Melting Completion (Liquidus), °C 1460
870
Melting Onset (Solidus), °C 1420
960
Specific Heat Capacity, J/kg-K 470
270
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
86
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
75

Otherwise Unclassified Properties

Density, g/cm3 7.8
10

Common Calculations

Stiffness to Weight: Axial, points 13
4.8
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 21
7.1 to 13
Strength to Weight: Bending, points 20
8.9 to 13
Thermal Shock Resistance, points 17
12 to 21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.040
0
Carbon (C), % 0 to 0.16
0
Iron (Fe), % 96.6 to 99.98
0
Manganese (Mn), % 0 to 1.7
0
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 0 to 0.5
13.8 to 16
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
84 to 86
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.1
0
Residuals, % 0
0 to 0.2