EN 1.8824 steel belongs to the iron alloys classification, while AWS BNi-2 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is EN 1.8824 steel and the bottom bar is AWS BNi-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
180
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 73
68
Tensile Strength: Ultimate (UTS), MPa 580
440

Thermal Properties

Latent Heat of Fusion, J/g 250
360
Melting Completion (Liquidus), °C 1460
1000
Melting Onset (Solidus), °C 1420
970
Specific Heat Capacity, J/kg-K 470
490
Thermal Expansion, µm/m-K 13
11

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
55
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.6
9.3
Embodied Energy, MJ/kg 21
130
Embodied Water, L/kg 48
230

Common Calculations

Stiffness to Weight: Axial, points 13
12
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 21
15
Strength to Weight: Bending, points 20
16
Thermal Shock Resistance, points 17
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.040
0 to 0.050
Boron (B), % 0
2.8 to 3.5
Carbon (C), % 0 to 0.16
0 to 0.060
Chromium (Cr), % 0
6.0 to 8.0
Cobalt (Co), % 0
0 to 0.1
Iron (Fe), % 96.6 to 99.98
2.5 to 3.5
Manganese (Mn), % 0 to 1.7
0
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 0 to 0.5
79.1 to 84.8
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0 to 0.5
4.0 to 5.0
Sulfur (S), % 0 to 0.010
0 to 0.020
Titanium (Ti), % 0 to 0.050
0 to 0.050
Vanadium (V), % 0 to 0.1
0
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5