EN 1.8824 Steel vs. AWS ENiCrCoMo-1

EN 1.8824 steel belongs to the iron alloys classification, while AWS ENiCrCoMo-1 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.8824 steel and the bottom bar is AWS ENiCrCoMo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 22
28
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
82
Tensile Strength: Ultimate (UTS), MPa 580
710

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
440
Thermal Expansion, µm/m-K 13
13

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
75
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 1.6
11
Embodied Energy, MJ/kg 21
140
Embodied Water, L/kg 48
340

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 21
23
Strength to Weight: Bending, points 20
21
Thermal Shock Resistance, points 17
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.040
0
Carbon (C), % 0 to 0.16
0.050 to 0.15
Chromium (Cr), % 0
21 to 26
Cobalt (Co), % 0
9.0 to 15
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 96.6 to 99.98
0 to 5.0
Manganese (Mn), % 0 to 1.7
0.3 to 2.5
Molybdenum (Mo), % 0 to 0.2
8.0 to 10
Nickel (Ni), % 0 to 0.5
38.6 to 61.7
Niobium (Nb), % 0 to 0.050
0 to 1.0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 0.75
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.1
0
Residuals, % 0
0 to 0.5