EN 1.8824 Steel vs. AWS ERNiCrMo-4

EN 1.8824 steel belongs to the iron alloys classification, while AWS ERNiCrMo-4 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.8824 steel and the bottom bar is AWS ERNiCrMo-4.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 22
28
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
84
Tensile Strength: Ultimate (UTS), MPa 580
790

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Melting Completion (Liquidus), °C 1460
1590
Melting Onset (Solidus), °C 1420
1530
Specific Heat Capacity, J/kg-K 470
410
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
70
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 1.6
13
Embodied Energy, MJ/kg 21
170
Embodied Water, L/kg 48
280

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 21
24
Strength to Weight: Bending, points 20
21
Thermal Shock Resistance, points 17
22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.040
0
Carbon (C), % 0 to 0.16
0 to 0.020
Chromium (Cr), % 0
14.5 to 16.5
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 96.6 to 99.98
4.0 to 7.0
Manganese (Mn), % 0 to 1.7
0 to 1.0
Molybdenum (Mo), % 0 to 0.2
15 to 17
Nickel (Ni), % 0 to 0.5
50 to 63.5
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 0.080
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.050
0
Tungsten (W), % 0
3.0 to 4.5
Vanadium (V), % 0 to 0.1
0 to 0.35
Residuals, % 0
0 to 0.5