EN 1.8824 Steel vs. Grade 17 Titanium

EN 1.8824 steel belongs to the iron alloys classification, while grade 17 titanium belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.8824 steel and the bottom bar is grade 17 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 22
27
Fatigue Strength, MPa 310
160
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 73
38
Shear Strength, MPa 370
180
Tensile Strength: Ultimate (UTS), MPa 580
270
Tensile Strength: Yield (Proof), MPa 440
210

Thermal Properties

Latent Heat of Fusion, J/g 250
420
Maximum Temperature: Mechanical, °C 400
320
Melting Completion (Liquidus), °C 1460
1660
Melting Onset (Solidus), °C 1420
1610
Specific Heat Capacity, J/kg-K 470
540
Thermal Conductivity, W/m-K 49
23
Thermal Expansion, µm/m-K 13
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
3.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
7.3

Otherwise Unclassified Properties

Density, g/cm3 7.8
4.5
Embodied Carbon, kg CO2/kg material 1.6
36
Embodied Energy, MJ/kg 21
600
Embodied Water, L/kg 48
230

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
68
Resilience: Unit (Modulus of Resilience), kJ/m3 530
220
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
35
Strength to Weight: Axial, points 21
17
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 13
9.3
Thermal Shock Resistance, points 17
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.040
0
Carbon (C), % 0 to 0.16
0 to 0.080
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 96.6 to 99.98
0 to 0.2
Manganese (Mn), % 0 to 1.7
0
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0 to 0.030
Oxygen (O), % 0
0 to 0.18
Palladium (Pd), % 0
0.040 to 0.080
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0 to 0.050
99.015 to 99.96
Vanadium (V), % 0 to 0.1
0
Residuals, % 0
0 to 0.4