EN 1.8824 Steel vs. Solder Alloy 502

EN 1.8824 steel belongs to the iron alloys classification, while solder alloy 502 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.8824 steel and the bottom bar is solder alloy 502.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
53
Elongation at Break, % 22
34
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 73
19
Tensile Strength: Ultimate (UTS), MPa 580
58

Thermal Properties

Latent Heat of Fusion, J/g 250
66
Melting Completion (Liquidus), °C 1460
350
Melting Onset (Solidus), °C 1420
220
Specific Heat Capacity, J/kg-K 470
230
Thermal Conductivity, W/m-K 49
47
Thermal Expansion, µm/m-K 13
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
12
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
15

Otherwise Unclassified Properties

Density, g/cm3 7.8
7.4
Embodied Carbon, kg CO2/kg material 1.6
15
Embodied Energy, MJ/kg 21
260

Common Calculations

Stiffness to Weight: Axial, points 13
4.0
Stiffness to Weight: Bending, points 24
17
Strength to Weight: Axial, points 21
2.2
Strength to Weight: Bending, points 20
4.5
Thermal Diffusivity, mm2/s 13
28
Thermal Shock Resistance, points 17
3.6

Alloy Composition

Aluminum (Al), % 0.020 to 0.040
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.080
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.16
0
Copper (Cu), % 0
3.5 to 4.5
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 96.6 to 99.98
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 0 to 1.7
0
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 0 to 0.5
0 to 0.010
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
0.8 to 1.2
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
93.8 to 95.7
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.1
0
Zinc (Zn), % 0
0 to 0.0010