EN 1.8824 Steel vs. C44300 Brass

EN 1.8824 steel belongs to the iron alloys classification, while C44300 brass belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.8824 steel and the bottom bar is C44300 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 73
41
Tensile Strength: Ultimate (UTS), MPa 580
350
Tensile Strength: Yield (Proof), MPa 440
120

Thermal Properties

Latent Heat of Fusion, J/g 250
180
Maximum Temperature: Mechanical, °C 400
140
Melting Completion (Liquidus), °C 1460
940
Melting Onset (Solidus), °C 1420
900
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 49
110
Thermal Expansion, µm/m-K 13
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
25
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
27

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
26
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 1.6
2.8
Embodied Energy, MJ/kg 21
46
Embodied Water, L/kg 48
330

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 530
65
Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 21
12
Strength to Weight: Bending, points 20
13
Thermal Diffusivity, mm2/s 13
35
Thermal Shock Resistance, points 17
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.040
0
Arsenic (As), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.16
0
Copper (Cu), % 0
70 to 73
Iron (Fe), % 96.6 to 99.98
0 to 0.060
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 0 to 1.7
0
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
0.9 to 1.2
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.1
0
Zinc (Zn), % 0
25.2 to 29.1
Residuals, % 0
0 to 0.4