MakeItFrom.com
Menu (ESC)

EN 1.8824 Steel vs. C71000 Copper-nickel

EN 1.8824 steel belongs to the iron alloys classification, while C71000 copper-nickel belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.8824 steel and the bottom bar is C71000 copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
130
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
49
Tensile Strength: Ultimate (UTS), MPa 580
320 to 560

Thermal Properties

Latent Heat of Fusion, J/g 250
230
Maximum Temperature: Mechanical, °C 400
240
Melting Completion (Liquidus), °C 1460
1200
Melting Onset (Solidus), °C 1420
1150
Specific Heat Capacity, J/kg-K 470
400
Thermal Conductivity, W/m-K 49
43
Thermal Expansion, µm/m-K 13
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
6.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
6.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
37
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.6
4.3
Embodied Energy, MJ/kg 21
63
Embodied Water, L/kg 48
290

Common Calculations

Stiffness to Weight: Axial, points 13
8.2
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 21
10 to 18
Strength to Weight: Bending, points 20
12 to 17
Thermal Diffusivity, mm2/s 13
12
Thermal Shock Resistance, points 17
12 to 20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.040
0
Carbon (C), % 0 to 0.16
0
Copper (Cu), % 0
73.5 to 80.5
Iron (Fe), % 96.6 to 99.98
0.5 to 1.0
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0 to 1.7
0 to 1.0
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 0 to 0.5
19 to 23
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.1
0
Zinc (Zn), % 0
0 to 1.0
Residuals, % 0
0 to 0.5