EN 1.8824 Steel vs. C71640 Copper-nickel

EN 1.8824 steel belongs to the iron alloys classification, while C71640 copper-nickel belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.8824 steel and the bottom bar is C71640 copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
140
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
52
Tensile Strength: Ultimate (UTS), MPa 580
490 to 630
Tensile Strength: Yield (Proof), MPa 440
190 to 460

Thermal Properties

Latent Heat of Fusion, J/g 250
240
Maximum Temperature: Mechanical, °C 400
260
Melting Completion (Liquidus), °C 1460
1180
Melting Onset (Solidus), °C 1420
1120
Specific Heat Capacity, J/kg-K 470
410
Thermal Conductivity, W/m-K 49
29
Thermal Expansion, µm/m-K 13
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
7.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
40
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.6
5.0
Embodied Energy, MJ/kg 21
73
Embodied Water, L/kg 48
280

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 530
130 to 750
Stiffness to Weight: Axial, points 13
8.7
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 21
15 to 20
Strength to Weight: Bending, points 20
16 to 18
Thermal Diffusivity, mm2/s 13
8.2
Thermal Shock Resistance, points 17
16 to 21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.040
0
Carbon (C), % 0 to 0.16
0
Copper (Cu), % 0
61.7 to 67.8
Iron (Fe), % 96.6 to 99.98
1.7 to 2.3
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0 to 1.7
1.5 to 2.5
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 0 to 0.5
29 to 32
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.1
0
Zinc (Zn), % 0
0 to 1.0
Residuals, % 0
0 to 0.5