EN 1.8824 Steel vs. C97300 Nickel Silver

EN 1.8824 steel belongs to the iron alloys classification, while C97300 nickel silver belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.8824 steel and the bottom bar is C97300 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 22
9.0
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
40
Tensile Strength: Ultimate (UTS), MPa 580
230
Tensile Strength: Yield (Proof), MPa 440
110

Thermal Properties

Latent Heat of Fusion, J/g 250
180
Maximum Temperature: Mechanical, °C 400
150
Melting Completion (Liquidus), °C 1460
1040
Melting Onset (Solidus), °C 1420
1010
Specific Heat Capacity, J/kg-K 470
370
Thermal Conductivity, W/m-K 49
29
Thermal Expansion, µm/m-K 13
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
6.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
6.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
30
Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 1.6
3.7
Embodied Energy, MJ/kg 21
59
Embodied Water, L/kg 48
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
18
Resilience: Unit (Modulus of Resilience), kJ/m3 530
59
Stiffness to Weight: Axial, points 13
7.0
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 21
7.6
Strength to Weight: Bending, points 20
9.8
Thermal Diffusivity, mm2/s 13
9.3
Thermal Shock Resistance, points 17
8.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.040
0 to 0.0050
Antimony (Sb), % 0
0 to 0.35
Carbon (C), % 0 to 0.16
0
Copper (Cu), % 0
53 to 58
Iron (Fe), % 96.6 to 99.98
0 to 1.5
Lead (Pb), % 0
8.0 to 11
Manganese (Mn), % 0 to 1.7
0
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 0 to 0.5
11 to 14
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.050
Silicon (Si), % 0 to 0.5
0 to 0.15
Sulfur (S), % 0 to 0.010
0 to 0.080
Tin (Sn), % 0
1.5 to 3.0
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.1
0
Zinc (Zn), % 0
17 to 25
Residuals, % 0
0 to 1.0