EN 1.8835 Steel vs. AISI 317LMN Stainless Steel

Both EN 1.8835 steel and AISI 317LMN stainless steel are iron alloys. They have 61% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.8835 steel and the bottom bar is AISI 317LMN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21
45
Fatigue Strength, MPa 310
250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 360
430
Tensile Strength: Ultimate (UTS), MPa 580
620
Tensile Strength: Yield (Proof), MPa 440
270

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
1020
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
24
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.6
4.8
Embodied Energy, MJ/kg 21
65
Embodied Water, L/kg 48
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
230
Resilience: Unit (Modulus of Resilience), kJ/m3 510
180
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21
22
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 13
3.8
Thermal Shock Resistance, points 17
14

Alloy Composition

Aluminum (Al), % 0.020 to 0.040
0
Carbon (C), % 0 to 0.16
0 to 0.030
Chromium (Cr), % 0
17 to 20
Iron (Fe), % 96.7 to 99.98
54.4 to 65.4
Manganese (Mn), % 0 to 1.7
0 to 2.0
Molybdenum (Mo), % 0 to 0.2
4.0 to 5.0
Nickel (Ni), % 0 to 0.5
13.5 to 17.5
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0.1 to 0.2
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0 to 0.5
0 to 0.75
Sulfur (S), % 0 to 0.0080
0 to 0.030
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.1
0