EN 1.8835 Steel vs. EN 1.1151 Steel

Both EN 1.8835 steel and EN 1.1151 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.8835 steel and the bottom bar is EN 1.1151 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
130 to 150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
21 to 26
Fatigue Strength, MPa 310
180 to 240
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 360
300 to 330
Tensile Strength: Ultimate (UTS), MPa 580
460 to 520
Tensile Strength: Yield (Proof), MPa 440
240 to 340

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
50
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 21
19
Embodied Water, L/kg 48
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
98 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 510
160 to 310
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
16 to 18
Strength to Weight: Bending, points 20
17 to 18
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 17
15 to 16

Alloy Composition

Aluminum (Al), % 0.020 to 0.040
0
Carbon (C), % 0 to 0.16
0.17 to 0.24
Chromium (Cr), % 0
0 to 0.4
Iron (Fe), % 96.7 to 99.98
97.7 to 99.43
Manganese (Mn), % 0 to 1.7
0.4 to 0.7
Molybdenum (Mo), % 0 to 0.2
0 to 0.1
Nickel (Ni), % 0 to 0.5
0 to 0.4
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.0080
0 to 0.035
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.1
0