EN 1.8835 Steel vs. SAE-AISI 1070 Steel

Both EN 1.8835 steel and SAE-AISI 1070 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.8835 steel and the bottom bar is SAE-AISI 1070 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190 to 230
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
10 to 13
Fatigue Strength, MPa 310
270 to 350
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Shear Strength, MPa 360
380 to 460
Tensile Strength: Ultimate (UTS), MPa 580
640 to 760
Tensile Strength: Yield (Proof), MPa 440
420 to 560

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
50
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
10
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
12

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 21
19
Embodied Water, L/kg 48
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
59 to 86
Resilience: Unit (Modulus of Resilience), kJ/m3 510
470 to 850
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
23 to 27
Strength to Weight: Bending, points 20
21 to 24
Thermal Diffusivity, mm2/s 13
14
Thermal Shock Resistance, points 17
21 to 25

Alloy Composition

Aluminum (Al), % 0.020 to 0.040
0
Carbon (C), % 0 to 0.16
0.65 to 0.75
Iron (Fe), % 96.7 to 99.98
98.3 to 98.8
Manganese (Mn), % 0 to 1.7
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.0080
0 to 0.050
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.1
0