EN 1.8835 Steel vs. S13800 Stainless Steel

Both EN 1.8835 steel and S13800 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.8835 steel and the bottom bar is S13800 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
290 to 480
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21
11 to 18
Fatigue Strength, MPa 310
410 to 870
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 360
610 to 1030
Tensile Strength: Ultimate (UTS), MPa 580
980 to 1730
Tensile Strength: Yield (Proof), MPa 440
660 to 1580

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
810
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
16
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
15
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
3.4
Embodied Energy, MJ/kg 21
46
Embodied Water, L/kg 48
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
150 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 510
1090 to 5490
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21
35 to 61
Strength to Weight: Bending, points 20
28 to 41
Thermal Diffusivity, mm2/s 13
4.3
Thermal Shock Resistance, points 17
33 to 58

Alloy Composition

Aluminum (Al), % 0.020 to 0.040
0.9 to 1.4
Carbon (C), % 0 to 0.16
0 to 0.050
Chromium (Cr), % 0
12.3 to 13.2
Iron (Fe), % 96.7 to 99.98
73.6 to 77.3
Manganese (Mn), % 0 to 1.7
0 to 0.2
Molybdenum (Mo), % 0 to 0.2
2.0 to 3.0
Nickel (Ni), % 0 to 0.5
7.5 to 8.5
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0 to 0.010
Phosphorus (P), % 0 to 0.020
0 to 0.010
Silicon (Si), % 0 to 0.5
0 to 0.1
Sulfur (S), % 0 to 0.0080
0 to 0.0080
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.1
0