EN 1.8881 Steel vs. EN 1.4826 Stainless Steel

Both EN 1.8881 steel and EN 1.4826 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.8881 steel and the bottom bar is EN 1.4826 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
150
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16
9.1
Fatigue Strength, MPa 460
140
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 830
500
Tensile Strength: Yield (Proof), MPa 710
260

Thermal Properties

Latent Heat of Fusion, J/g 260
310
Maximum Temperature: Mechanical, °C 420
950
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 40
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.1
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 9.3
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 3.7
17
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.9
3.3
Embodied Energy, MJ/kg 26
47
Embodied Water, L/kg 54
160

Common Calculations

PREN (Pitting Resistance) 2.0
23
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
39
Resilience: Unit (Modulus of Resilience), kJ/m3 1320
170
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 29
18
Strength to Weight: Bending, points 25
18
Thermal Diffusivity, mm2/s 11
3.7
Thermal Shock Resistance, points 24
11

Alloy Composition

Boron (B), % 0 to 0.0050
0
Carbon (C), % 0 to 0.2
0.3 to 0.5
Chromium (Cr), % 0 to 1.5
21 to 23
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 91.9 to 100
60.4 to 68.7
Manganese (Mn), % 0 to 1.7
0 to 2.0
Molybdenum (Mo), % 0 to 0.7
0 to 0.5
Nickel (Ni), % 0 to 2.5
9.0 to 11
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.8
1.0 to 2.5
Sulfur (S), % 0 to 0.0080
0 to 0.030
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.12
0
Zirconium (Zr), % 0 to 0.15
0