EN 1.8881 Steel vs. EN 1.8895 Steel

Both EN 1.8881 steel and EN 1.8895 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.8881 steel and the bottom bar is EN 1.8895 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
120
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 16
26
Fatigue Strength, MPa 460
220
Impact Strength: V-Notched Charpy, J 90
46
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 510
260
Tensile Strength: Ultimate (UTS), MPa 830
400
Tensile Strength: Yield (Proof), MPa 710
300

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
49
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 9.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 3.7
2.2
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.6
Embodied Energy, MJ/kg 26
21
Embodied Water, L/kg 54
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
96
Resilience: Unit (Modulus of Resilience), kJ/m3 1320
240
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 29
14
Strength to Weight: Bending, points 25
15
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 24
12

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Boron (B), % 0 to 0.0050
0
Carbon (C), % 0 to 0.2
0 to 0.13
Chromium (Cr), % 0 to 1.5
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 91.9 to 100
97 to 99.98
Manganese (Mn), % 0 to 1.7
0 to 1.5
Molybdenum (Mo), % 0 to 0.7
0 to 0.2
Nickel (Ni), % 0 to 2.5
0 to 0.3
Niobium (Nb), % 0 to 0.060
0 to 0.050
Nitrogen (N), % 0 to 0.015
0 to 0.020
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.8
0 to 0.5
Sulfur (S), % 0 to 0.0080
0 to 0.030
Titanium (Ti), % 0 to 0.050
0 to 0.050
Vanadium (V), % 0 to 0.12
0 to 0.080
Zirconium (Zr), % 0 to 0.15
0