EN 1.8881 Steel vs. N08810 Stainless Steel

Both EN 1.8881 steel and N08810 stainless steel are iron alloys. They have 49% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.8881 steel and the bottom bar is N08810 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16
33
Fatigue Strength, MPa 460
160
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 510
340
Tensile Strength: Ultimate (UTS), MPa 830
520
Tensile Strength: Yield (Proof), MPa 710
200

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Maximum Temperature: Mechanical, °C 420
1100
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
12
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.1
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 9.3
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 3.7
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.9
5.3
Embodied Energy, MJ/kg 26
76
Embodied Water, L/kg 54
200

Common Calculations

PREN (Pitting Resistance) 2.0
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
140
Resilience: Unit (Modulus of Resilience), kJ/m3 1320
100
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 29
18
Strength to Weight: Bending, points 25
18
Thermal Diffusivity, mm2/s 11
3.0
Thermal Shock Resistance, points 24
13

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Boron (B), % 0 to 0.0050
0
Carbon (C), % 0 to 0.2
0.050 to 0.1
Chromium (Cr), % 0 to 1.5
19 to 23
Copper (Cu), % 0 to 0.3
0 to 0.75
Iron (Fe), % 91.9 to 100
39.5 to 50.7
Manganese (Mn), % 0 to 1.7
0 to 1.5
Molybdenum (Mo), % 0 to 0.7
0
Nickel (Ni), % 0 to 2.5
30 to 35
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0 to 0.8
0 to 1.0
Sulfur (S), % 0 to 0.0080
0 to 0.015
Titanium (Ti), % 0 to 0.050
0.15 to 0.6
Vanadium (V), % 0 to 0.12
0
Zirconium (Zr), % 0 to 0.15
0