EN 1.8881 Steel vs. Z21721 Zinc

EN 1.8881 steel belongs to the iron alloys classification, while Z21721 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.8881 steel and the bottom bar is Z21721 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Elongation at Break, % 16
40
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 73
35
Tensile Strength: Ultimate (UTS), MPa 830
150
Tensile Strength: Yield (Proof), MPa 710
120

Thermal Properties

Latent Heat of Fusion, J/g 260
110
Maximum Temperature: Mechanical, °C 420
90
Melting Completion (Liquidus), °C 1460
410
Melting Onset (Solidus), °C 1420
390
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 40
110
Thermal Expansion, µm/m-K 13
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.1
27
Electrical Conductivity: Equal Weight (Specific), % IACS 9.3
37

Otherwise Unclassified Properties

Base Metal Price, % relative 3.7
11
Density, g/cm3 7.8
6.6
Embodied Carbon, kg CO2/kg material 1.9
2.8
Embodied Energy, MJ/kg 26
53
Embodied Water, L/kg 54
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
57
Resilience: Unit (Modulus of Resilience), kJ/m3 1320
88
Stiffness to Weight: Axial, points 13
7.3
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 29
6.4
Strength to Weight: Bending, points 25
9.6
Thermal Diffusivity, mm2/s 11
44
Thermal Shock Resistance, points 24
4.8

Alloy Composition

Aluminum (Al), % 0
0 to 0.0020
Boron (B), % 0 to 0.0050
0
Cadmium (Cd), % 0
0 to 0.070
Carbon (C), % 0 to 0.2
0
Chromium (Cr), % 0 to 1.5
0
Copper (Cu), % 0 to 0.3
0 to 0.0050
Iron (Fe), % 91.9 to 100
0 to 0.010
Lead (Pb), % 0
0 to 1.0
Manganese (Mn), % 0 to 1.7
0
Molybdenum (Mo), % 0 to 0.7
0
Nickel (Ni), % 0 to 2.5
0
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.8
0
Sulfur (S), % 0 to 0.0080
0
Titanium (Ti), % 0 to 0.050
0 to 0.020
Vanadium (V), % 0 to 0.12
0
Zinc (Zn), % 0
98.9 to 100
Zirconium (Zr), % 0 to 0.15
0