EN 1.8888 Steel vs. EN 1.3536 Steel

Both EN 1.8888 steel and EN 1.3536 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.8888 steel and the bottom bar is EN 1.3536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 830
660

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 420
440
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
41
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.1
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 9.3
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 3.7
2.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.6
Embodied Energy, MJ/kg 26
21
Embodied Water, L/kg 54
55

Common Calculations

PREN (Pitting Resistance) 2.0
2.8
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 29
23
Strength to Weight: Bending, points 25
22
Thermal Diffusivity, mm2/s 11
11
Thermal Shock Resistance, points 24
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Boron (B), % 0 to 0.0050
0
Carbon (C), % 0 to 0.2
0.93 to 1.1
Chromium (Cr), % 0 to 1.5
1.7 to 2.0
Copper (Cu), % 0 to 0.3
0 to 0.3
Iron (Fe), % 91.9 to 100
96 to 97.4
Manganese (Mn), % 0 to 1.7
0.6 to 0.8
Molybdenum (Mo), % 0 to 0.7
0.2 to 0.35
Nickel (Ni), % 0 to 2.5
0
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.015
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0 to 0.8
0.15 to 0.45
Sulfur (S), % 0 to 0.0050
0 to 0.030
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.12
0
Zirconium (Zr), % 0 to 0.15
0