EN 1.8935 Steel vs. AISI 431 Stainless Steel

Both EN 1.8935 steel and AISI 431 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.8935 steel and the bottom bar is AISI 431 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
250
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
15 to 17
Fatigue Strength, MPa 330
430 to 610
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 400
550 to 840
Tensile Strength: Ultimate (UTS), MPa 640
890 to 1380
Tensile Strength: Yield (Proof), MPa 490
710 to 1040

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
850
Melting Completion (Liquidus), °C 1460
1510
Melting Onset (Solidus), °C 1420
1450
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 46
26
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
9.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.7
2.2
Embodied Energy, MJ/kg 24
31
Embodied Water, L/kg 51
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
140 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 640
1270 to 2770
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
32 to 50
Strength to Weight: Bending, points 21
27 to 36
Thermal Diffusivity, mm2/s 12
7.0
Thermal Shock Resistance, points 19
28 to 43

Alloy Composition

Aluminum (Al), % 0.020 to 0.050
0
Carbon (C), % 0 to 0.2
0 to 0.2
Chromium (Cr), % 0 to 0.3
15 to 17
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 95.2 to 98.9
78.2 to 83.8
Manganese (Mn), % 1.1 to 1.7
0 to 1.0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.8
1.3 to 2.5
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.025
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.2
0