EN 1.8935 Steel vs. EN 1.1203 Steel

Both EN 1.8935 steel and EN 1.1203 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.8935 steel and the bottom bar is EN 1.1203 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200 to 230
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
12 to 15
Fatigue Strength, MPa 330
210 to 310
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Shear Strength, MPa 400
420 to 480
Tensile Strength: Ultimate (UTS), MPa 640
690 to 780
Tensile Strength: Yield (Proof), MPa 490
340 to 480

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
48
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.4
Embodied Energy, MJ/kg 24
19
Embodied Water, L/kg 51
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
69 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 640
310 to 610
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
25 to 28
Strength to Weight: Bending, points 21
22 to 24
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 19
22 to 25

Alloy Composition

Aluminum (Al), % 0.020 to 0.050
0
Carbon (C), % 0 to 0.2
0.52 to 0.6
Chromium (Cr), % 0 to 0.3
0 to 0.4
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 95.2 to 98.9
97.1 to 98.9
Manganese (Mn), % 1.1 to 1.7
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.1
0 to 0.1
Nickel (Ni), % 0 to 0.8
0 to 0.4
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.025
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.6
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.035
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.2
0