EN 1.8935 Steel vs. EN 1.8915 Steel

Both EN 1.8935 steel and EN 1.8915 steel are iron alloys. Both are furnished in the normalized condition. Their average alloy composition is basically identical.

For each property being compared, the top bar is EN 1.8935 steel and the bottom bar is EN 1.8915 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
19
Fatigue Strength, MPa 330
340
Impact Strength: V-Notched Charpy, J 71
79
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 400
400
Tensile Strength: Ultimate (UTS), MPa 640
640
Tensile Strength: Yield (Proof), MPa 490
490

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
46
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
2.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.7
Embodied Energy, MJ/kg 24
24
Embodied Water, L/kg 51
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
110
Resilience: Unit (Modulus of Resilience), kJ/m3 640
640
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
23
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 12
12
Thermal Shock Resistance, points 19
19

Alloy Composition

Aluminum (Al), % 0.020 to 0.050
0.020 to 0.050
Carbon (C), % 0 to 0.2
0 to 0.2
Chromium (Cr), % 0 to 0.3
0 to 0.3
Copper (Cu), % 0 to 0.7
0 to 0.7
Iron (Fe), % 95.2 to 98.9
95.2 to 98.9
Manganese (Mn), % 1.1 to 1.7
1.1 to 1.7
Molybdenum (Mo), % 0 to 0.1
0 to 0.1
Nickel (Ni), % 0 to 0.8
0 to 0.8
Niobium (Nb), % 0 to 0.050
0 to 0.050
Nitrogen (N), % 0 to 0.025
0 to 0.025
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.6
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.0080
Titanium (Ti), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0 to 0.2
0 to 0.2