EN 1.8946 Steel vs. EN 1.5680 Steel
Both EN 1.8946 steel and EN 1.5680 steel are iron alloys. They have a very high 95% of their average alloy composition in common.
For each property being compared, the top bar is EN 1.8946 steel and the bottom bar is EN 1.5680 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 16 | |
| 23 |
| Fatigue Strength, MPa | 260 | |
| 310 |
| Impact Strength: V-Notched Charpy, J | 30 | |
| 71 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 350 | |
| 390 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 420 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 43 | |
| 48 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.6 | |
| 7.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 8.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.7 | |
| 5.0 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 1.9 |
| Embodied Energy, MJ/kg | 23 | |
| 26 |
| Embodied Water, L/kg | 51 | |
| 55 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 82 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 410 | |
| 510 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 20 | |
| 22 |
| Strength to Weight: Bending, points | 20 | |
| 20 |
| Thermal Diffusivity, mm2/s | 12 | |
| 13 |
| Thermal Shock Resistance, points | 17 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.030 | |
| 0 |
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0.25 to 1.4 | |
| 0 |
| Copper (Cu), % | 0.2 to 0.6 | |
| 0 |
| Iron (Fe), % | 94.8 to 99.5 | |
| 93.4 to 95 |
| Manganese (Mn), % | 0 to 1.1 | |
| 0.3 to 0.8 |
| Nickel (Ni), % | 0 to 0.7 | |
| 4.8 to 5.3 |
| Niobium (Nb), % | 0 to 0.065 | |
| 0 |
| Phosphorus (P), % | 0.050 to 0.16 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.8 | |
| 0 to 0.35 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.0050 |
| Titanium (Ti), % | 0 to 0.12 | |
| 0 |
| Vanadium (V), % | 0 to 0.14 | |
| 0 to 0.050 |