EN 2.4663 Nickel vs. Z21721 Zinc

EN 2.4663 nickel belongs to the nickel alloys classification, while Z21721 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 2.4663 nickel and the bottom bar is Z21721 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
87
Elongation at Break, % 40
40
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 81
35
Tensile Strength: Ultimate (UTS), MPa 780
150
Tensile Strength: Yield (Proof), MPa 310
120

Thermal Properties

Latent Heat of Fusion, J/g 320
110
Maximum Temperature: Mechanical, °C 1010
90
Melting Completion (Liquidus), °C 1430
410
Melting Onset (Solidus), °C 1380
390
Specific Heat Capacity, J/kg-K 450
390
Thermal Conductivity, W/m-K 13
110
Thermal Expansion, µm/m-K 12
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
27
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
37

Otherwise Unclassified Properties

Base Metal Price, % relative 75
11
Density, g/cm3 8.6
6.6
Embodied Carbon, kg CO2/kg material 11
2.8
Embodied Energy, MJ/kg 140
53
Embodied Water, L/kg 350
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 250
57
Resilience: Unit (Modulus of Resilience), kJ/m3 230
88
Stiffness to Weight: Axial, points 14
7.3
Stiffness to Weight: Bending, points 23
22
Strength to Weight: Axial, points 25
6.4
Strength to Weight: Bending, points 22
9.6
Thermal Diffusivity, mm2/s 3.5
44
Thermal Shock Resistance, points 22
4.8

Alloy Composition

Aluminum (Al), % 0.7 to 1.4
0 to 0.0020
Boron (B), % 0 to 0.0060
0
Cadmium (Cd), % 0
0 to 0.070
Carbon (C), % 0.050 to 0.1
0
Chromium (Cr), % 20 to 23
0
Cobalt (Co), % 11 to 14
0
Copper (Cu), % 0 to 0.5
0 to 0.0050
Iron (Fe), % 0 to 2.0
0 to 0.010
Lead (Pb), % 0
0 to 1.0
Manganese (Mn), % 0 to 0.2
0
Molybdenum (Mo), % 8.5 to 10
0
Nickel (Ni), % 48 to 59.6
0
Phosphorus (P), % 0 to 0.010
0
Silicon (Si), % 0 to 0.2
0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0.2 to 0.6
0 to 0.020
Zinc (Zn), % 0
98.9 to 100