EN 2.4815 Cast Nickel vs. AWS BNi-10

Both EN 2.4815 cast nickel and AWS BNi-10 are nickel alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 79% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 2.4815 cast nickel and the bottom bar is AWS BNi-10.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
76
Tensile Strength: Ultimate (UTS), MPa 460
600

Thermal Properties

Latent Heat of Fusion, J/g 330
330
Melting Completion (Liquidus), °C 1510
1110
Melting Onset (Solidus), °C 1450
970
Specific Heat Capacity, J/kg-K 470
440
Thermal Expansion, µm/m-K 10
11

Otherwise Unclassified Properties

Base Metal Price, % relative 47
80
Density, g/cm3 8.3
9.4
Embodied Carbon, kg CO2/kg material 7.9
11
Embodied Energy, MJ/kg 110
160
Embodied Water, L/kg 230
230

Common Calculations

Stiffness to Weight: Axial, points 13
12
Stiffness to Weight: Bending, points 23
21
Strength to Weight: Axial, points 15
18
Strength to Weight: Bending, points 16
17
Thermal Shock Resistance, points 17
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.050
Boron (B), % 0
2.0 to 3.0
Carbon (C), % 0.35 to 0.65
0.4 to 0.55
Chromium (Cr), % 12 to 18
10 to 13
Cobalt (Co), % 0
0 to 0.1
Iron (Fe), % 9.8 to 28.7
2.5 to 4.5
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 1.0
0
Nickel (Ni), % 58 to 66
57.2 to 67.1
Phosphorus (P), % 0 to 0.040
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 1.0 to 2.5
3.0 to 4.0
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Tungsten (W), % 0
15 to 17
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5