EN 2.4815 Cast Nickel vs. AWS BNi-5

Both EN 2.4815 cast nickel and AWS BNi-5 are nickel alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 79% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 2.4815 cast nickel and the bottom bar is AWS BNi-5.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
72
Tensile Strength: Ultimate (UTS), MPa 460
470

Thermal Properties

Latent Heat of Fusion, J/g 330
470
Melting Completion (Liquidus), °C 1510
1140
Melting Onset (Solidus), °C 1450
1080
Specific Heat Capacity, J/kg-K 470
510
Thermal Expansion, µm/m-K 10
12

Otherwise Unclassified Properties

Base Metal Price, % relative 47
55
Density, g/cm3 8.3
7.7
Embodied Carbon, kg CO2/kg material 7.9
8.9
Embodied Energy, MJ/kg 110
130
Embodied Water, L/kg 230
260

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 15
17
Strength to Weight: Bending, points 16
17
Thermal Shock Resistance, points 17
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.050
Boron (B), % 0
0 to 0.030
Carbon (C), % 0.35 to 0.65
0 to 0.060
Chromium (Cr), % 12 to 18
18.5 to 19.5
Cobalt (Co), % 0
0 to 0.1
Iron (Fe), % 9.8 to 28.7
0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 1.0
0
Nickel (Ni), % 58 to 66
69.1 to 71.8
Phosphorus (P), % 0 to 0.040
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 1.0 to 2.5
9.8 to 10.5
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5