EN 2.4815 Cast Nickel vs. EN 1.4378 Stainless Steel
EN 2.4815 cast nickel belongs to the nickel alloys classification, while EN 1.4378 stainless steel belongs to the iron alloys. They have a modest 39% of their average alloy composition in common, which, by itself, doesn't mean much. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 2.4815 cast nickel and the bottom bar is EN 1.4378 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 3.4 | |
| 14 to 34 |
| Fatigue Strength, MPa | 89 | |
| 340 to 550 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 74 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 460 | |
| 760 to 1130 |
| Tensile Strength: Yield (Proof), MPa | 220 | |
| 430 to 970 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 910 |
| Melting Completion (Liquidus), °C | 1510 | |
| 1390 |
| Melting Onset (Solidus), °C | 1450 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 10 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 47 | |
| 12 |
| Density, g/cm3 | 8.3 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 2.7 |
| Embodied Energy, MJ/kg | 110 | |
| 39 |
| Embodied Water, L/kg | 230 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 | |
| 150 to 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 | |
| 470 to 2370 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 15 | |
| 28 to 41 |
| Strength to Weight: Bending, points | 16 | |
| 24 to 31 |
| Thermal Shock Resistance, points | 17 | |
| 16 to 23 |
Alloy Composition
| Carbon (C), % | 0.35 to 0.65 | |
| 0 to 0.080 |
| Chromium (Cr), % | 12 to 18 | |
| 17 to 19 |
| Iron (Fe), % | 9.8 to 28.7 | |
| 61.2 to 69 |
| Manganese (Mn), % | 0 to 2.0 | |
| 11.5 to 14.5 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 58 to 66 | |
| 2.3 to 3.7 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.4 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.060 |
| Silicon (Si), % | 1.0 to 2.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |