EN 2.4856 Nickel vs. Reactor Grade Zirconium
EN 2.4856 nickel belongs to the nickel alloys classification, while reactor grade zirconium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is EN 2.4856 nickel and the bottom bar is reactor grade zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 98 |
| Elongation at Break, % | 28 | |
| 21 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 79 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 880 | |
| 330 |
| Tensile Strength: Yield (Proof), MPa | 430 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 270 |
| Thermal Conductivity, W/m-K | 10 | |
| 22 |
| Thermal Expansion, µm/m-K | 11 | |
| 5.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.6 | |
| 6.5 |
| Embodied Water, L/kg | 290 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 | |
| 56 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 440 | |
| 130 |
| Stiffness to Weight: Axial, points | 13 | |
| 8.4 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 28 | |
| 14 |
| Strength to Weight: Bending, points | 24 | |
| 16 |
| Thermal Diffusivity, mm2/s | 2.7 | |
| 13 |
| Thermal Shock Resistance, points | 29 | |
| 41 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.4 | |
| 0 |
| Carbon (C), % | 0.030 to 0.1 | |
| 0 |
| Chromium (Cr), % | 20 to 23 | |
| 0 |
| Cobalt (Co), % | 0 to 1.0 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 0 to 5.0 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Molybdenum (Mo), % | 8.0 to 10 | |
| 0 |
| Nickel (Ni), % | 58 to 68.8 | |
| 0 |
| Niobium (Nb), % | 3.2 to 4.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Titanium (Ti), % | 0 to 0.4 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 99.7 to 100 |
| Residuals, % | 0 | |
| 0 to 0.27 |