EN 2.4879 Cast Nickel vs. SAE-AISI 1018 Steel
EN 2.4879 cast nickel belongs to the nickel alloys classification, while SAE-AISI 1018 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 2.4879 cast nickel and the bottom bar is SAE-AISI 1018 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 3.4 | |
| 17 to 27 |
| Fatigue Strength, MPa | 110 | |
| 180 to 270 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 80 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 490 | |
| 430 to 480 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 240 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1150 | |
| 400 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 52 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 55 | |
| 1.8 |
| Density, g/cm3 | 8.5 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 1.4 |
| Embodied Energy, MJ/kg | 120 | |
| 18 |
| Embodied Water, L/kg | 270 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 | |
| 75 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 150 to 430 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 16 | |
| 15 to 17 |
| Strength to Weight: Bending, points | 16 | |
| 16 to 17 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 14 |
| Thermal Shock Resistance, points | 13 | |
| 14 to 15 |
Alloy Composition
| Carbon (C), % | 0.35 to 0.55 | |
| 0.15 to 0.2 |
| Chromium (Cr), % | 27 to 30 | |
| 0 |
| Iron (Fe), % | 9.4 to 20.7 | |
| 98.8 to 99.25 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 47 to 50 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 1.0 to 2.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.050 |
| Tungsten (W), % | 4.0 to 6.0 | |
| 0 |