EN 2.4952 Nickel vs. AISI 410Cb Stainless Steel
EN 2.4952 nickel belongs to the nickel alloys classification, while AISI 410Cb stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 2.4952 nickel and the bottom bar is AISI 410Cb stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 17 | |
| 15 |
| Fatigue Strength, MPa | 370 | |
| 180 to 460 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Reduction in Area, % | 14 | |
| 50 to 51 |
| Shear Modulus, GPa | 74 | |
| 76 |
| Shear Strength, MPa | 700 | |
| 340 to 590 |
| Tensile Strength: Ultimate (UTS), MPa | 1150 | |
| 550 to 960 |
| Tensile Strength: Yield (Proof), MPa | 670 | |
| 310 to 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 730 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1450 |
| Melting Onset (Solidus), °C | 1300 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 12 | |
| 27 |
| Thermal Expansion, µm/m-K | 13 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.4 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.5 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 55 | |
| 7.5 |
| Density, g/cm3 | 8.3 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 9.8 | |
| 2.0 |
| Embodied Energy, MJ/kg | 140 | |
| 29 |
| Embodied Water, L/kg | 290 | |
| 97 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 70 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1180 | |
| 240 to 1600 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 38 | |
| 20 to 35 |
| Strength to Weight: Bending, points | 29 | |
| 19 to 28 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 7.3 |
| Thermal Shock Resistance, points | 33 | |
| 20 to 35 |
Alloy Composition
| Aluminum (Al), % | 1.0 to 1.8 | |
| 0 |
| Boron (B), % | 0 to 0.0080 | |
| 0 |
| Carbon (C), % | 0.040 to 0.1 | |
| 0 to 0.18 |
| Chromium (Cr), % | 18 to 21 | |
| 11 to 13 |
| Cobalt (Co), % | 0 to 1.0 | |
| 0 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 |
| Iron (Fe), % | 0 to 1.5 | |
| 84.5 to 89 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 65 to 79.2 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 0.050 to 0.3 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Titanium (Ti), % | 1.8 to 2.7 | |
| 0 |