EN 2.4964 Cobalt vs. 2011 Aluminum
EN 2.4964 cobalt belongs to the cobalt alloys classification, while 2011 aluminum belongs to the aluminum alloys. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 2.4964 cobalt and the bottom bar is 2011 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 71 |
| Elongation at Break, % | 40 | |
| 8.5 to 18 |
| Fatigue Strength, MPa | 220 | |
| 74 to 120 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 86 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 960 | |
| 310 to 420 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 140 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 390 |
| Melting Completion (Liquidus), °C | 1630 | |
| 640 |
| Melting Onset (Solidus), °C | 1550 | |
| 540 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 870 |
| Thermal Conductivity, W/m-K | 15 | |
| 140 to 170 |
| Thermal Expansion, µm/m-K | 12 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.9 | |
| 35 to 45 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.8 | |
| 100 to 130 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.6 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 9.8 | |
| 7.9 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 450 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 310 | |
| 29 to 52 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 340 | |
| 140 to 680 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 44 |
| Strength to Weight: Axial, points | 28 | |
| 27 to 37 |
| Strength to Weight: Bending, points | 23 | |
| 32 to 40 |
| Thermal Diffusivity, mm2/s | 3.9 | |
| 51 to 64 |
| Thermal Shock Resistance, points | 25 | |
| 14 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 91.3 to 94.6 |
| Bismuth (Bi), % | 0 | |
| 0.2 to 0.6 |
| Carbon (C), % | 0.050 to 0.15 | |
| 0 |
| Chromium (Cr), % | 19 to 21 | |
| 0 |
| Cobalt (Co), % | 46.4 to 58 | |
| 0 |
| Copper (Cu), % | 0 | |
| 5.0 to 6.0 |
| Iron (Fe), % | 0 to 3.0 | |
| 0 to 0.7 |
| Lead (Pb), % | 0 | |
| 0.2 to 0.6 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Nickel (Ni), % | 9.0 to 11 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tungsten (W), % | 14 to 16 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.3 |
| Residuals, % | 0 | |
| 0 to 0.15 |