EN 2.4964 Cobalt vs. 5754 Aluminum

EN 2.4964 cobalt belongs to the cobalt alloys classification, while 5754 aluminum belongs to the aluminum alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 2.4964 cobalt and the bottom bar is 5754 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
68
Elongation at Break, % 40
2.0 to 19
Fatigue Strength, MPa 220
66 to 140
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 86
26
Tensile Strength: Ultimate (UTS), MPa 960
200 to 330
Tensile Strength: Yield (Proof), MPa 390
80 to 280

Thermal Properties

Latent Heat of Fusion, J/g 290
400
Melting Completion (Liquidus), °C 1630
650
Melting Onset (Solidus), °C 1550
600
Specific Heat Capacity, J/kg-K 400
900
Thermal Conductivity, W/m-K 15
130
Thermal Expansion, µm/m-K 12
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
33
Electrical Conductivity: Equal Weight (Specific), % IACS 1.8
110

Otherwise Unclassified Properties

Density, g/cm3 9.6
2.7
Embodied Carbon, kg CO2/kg material 9.8
8.7
Embodied Energy, MJ/kg 140
150
Embodied Water, L/kg 450
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 310
6.1 to 32
Resilience: Unit (Modulus of Resilience), kJ/m3 340
47 to 580
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 21
50
Strength to Weight: Axial, points 28
21 to 34
Strength to Weight: Bending, points 23
28 to 39
Thermal Diffusivity, mm2/s 3.9
54
Thermal Shock Resistance, points 25
8.9 to 14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
94.2 to 97.4
Carbon (C), % 0.050 to 0.15
0
Chromium (Cr), % 19 to 21
0 to 0.3
Cobalt (Co), % 46.4 to 58
0
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 0 to 3.0
0 to 0.4
Magnesium (Mg), % 0
2.6 to 3.6
Manganese (Mn), % 0 to 2.0
0 to 0.5
Nickel (Ni), % 9.0 to 11
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0
0 to 0.15
Tungsten (W), % 14 to 16
0
Zinc (Zn), % 0
0 to 0.2
Residuals, % 0
0 to 0.15